- TRIBALOY® T-800®
TRIBALOY® T-800®
Product Information
Tribaloy® T-800® is a cobalt-chromium-molybdenum alloy which inhibits galling between sliding surfaces where lubrication is difficult. The microstructure of Tribaloy® T-800 consists of about 50% of the hard intermetallic Laves phase dispersed in a softer cobalt alloy matrix. This provides the material with exceptional metal to metal wear bearing properties. The high levels of molybdenum and chromium present favors the formation of the high hardness Laves phase and also provides a high level of corrosion resistance. The Laves phase itself has a 2840°F melting point, which helps Tribaloy T-800 retain its wear resistance to high temperatures. Deposit hardness is in the range of Rc 54-62. Wire diameters 0.035", 0.045" and 0.062" are available as straight cut lengths 17" standard. Shapes are available per customer requirements.
Common Trade Names
Tribaloy®
Inventory
Tribaloy® T-800® Welding Products
Specifications
HARDFACING MATERIALS SNECMA: DMR 34.071, B50TF193
Chemical Composition, %
| Cr | Ni+Fe | Mo | Co | C | N | O | Si | P | S | |
|---|---|---|---|---|---|---|---|---|---|---|
| MIN | 16.50 | -- | 27.00 | -- | -- | -- | -- | 3.00 | -- | -- |
| MAX | 18.50 | 3.00 | 30.00 | Balance | 0.08 | 0.07 | 0.05 | 3.80 | 0.03 | 0.03 |
Features
- Low coefficient of friction
Applications
- Hardfacing of notches in jet engine turbine blades
Physical Properties
Density: 0.312 lb/in3 Melting Range: 6.8 in/in°F x 106
Physical Properties
| Ultimate Compressive Strength, ksi | 258 |
| Modulus of Elasticity Dynamic, psi x 10-6 | 352 |
| Fracture Toughness ksi √in | 17 |
Hot Hardness
| Temperature, °F ksi | 800 | 1000 | 1200 | 1400 |
| Hot Hardness, DPH | 17 | 308 | 659 | 622 |